MegaZemin Z502

• Its anti-slip property is increased thanks to its textured surface.
• It has high resistance to mechanical effects.
• It has high chemical resistance.
• It is waterproof.
• It is aesthetic thanks to its wide color choice and textured surface.
• It is long-lasting and easy to clean.
• It is solvent free, environmentally friendly.

Usage Areas

• MegaZemin Z502 is used in spaces exposed to moderate to severe mechanical influences such as multi-storey and underground car parks, storage areas, maintenance hangars; in places where chemical resistance is desired such as laboratories and non-slip is required in pedestrian walking areas, easy maintenance and cleaning is important and that is not exposed to sunlight. It is used indoors, on horizontal surfaces.
  

  ---

  Technical Informations

  • Performance

    Technicial Specificationsa. Chemical Structure: Epoxy resin based
    b. Amount of non-volatile solids : 100% by volume and weight
    c. Density (Component A): ~ 1.50 kg/l
    d. Density (Component B): ~ 1.00 kg/l
    e. Density (Mixture): ~ 1.45 kg/l
    f. Color: RAL swatch chart colors and special colors

    Mixing RatioComponent A (21.4 kg) and Component B (3.6 kg) must be completely mixed.

    ConsumptionPackagingMegaZemin Z502; Net 21,4 kg of Component A and 3,6 kg of Component B are offered as a set in tin buckets.

    Reference StandardsApprovals / Standarts
    • TS EN 13813
    • TS EN 1504-2
    Ministry of Public Works Position No.
    • Ministry of Public Works Position No.: 04.379/H04

    Quality Certificates
    • CE

  ---

  Technical Informations

  • Application Surfaces
    Indoor Floor;
    • Concrete ( MegaFilm A502 or MegaFilm A504 primer applied)

    Surface Preparation:
    • The surface should be dry, clean, firm and free of dust; oil, dirt or materials that prevent adhesion should be cleaned from the surface; substances such as mortar, cement residues should be scraped.
    • Before the primer application on the surface, an open porous structure should be created on the cement top layer by using surface abrasive equipment (shotblast, rototiger, etc.). Emerging dust must be cleaned with an industrial broom.
    • The abraded concrete surface must have a minimum compressive strength of 25 N/mm 2 and a tensile strength of minimum 1,5/mm 2 .
    • Before application, it must be ensured to meet the requirements for surface humidity, relative humidity and dew point. Otherwise, the desired performance criteria cannot be obtained from the product as a result of the carbonation reaction that will occur on the surface.
    • The moisture content of the surface should be a maximum of 4%.
    • Relative humidity should be a maximum of 80%.
    • Before and after the application, the dew point should be above +3°C in order to prevent the formation of condensation.
    • New concrete structures should be left to dry for a minimum of 28 days.
    • MegaTamir Epo or MegaTamir EpoGrout Repair should be made for repairing surface defects with a depth of more than 1 cm before 6 – 8 hours
    • After surface cleaning, it should be primed as single or double with MegaFilm A504 primerdepending on the condition of the surface on the subsiding grounds with waterproof applications were performed with Megafilm A502 primer in order to increase the bond strength and balance surface absorbancy or to meet the requirements of the waterproofing regulation on buildings and on the places having moisture barrier constructed. Depending on the porosity and structure of the surface, floor leveling can be done with the addition of filler.
    • Minimum 20 minutes after the primer application, before curing of the primer, the adhesion strength of the floor covering to be applied after it should be increased by sandblasting with suitable filler until the product reaches saturation. Please refer to the expenditure/consumption table for the recommended amount of filler.
    • In order to go into the MegaZemin Z501 application, the sandblasted primer must have gained its hardness. Please refer to the technical data sheet of the primer used, as the temperature and the opening time may change.
    • After primer sandblasting, the non-adhering fillings should be removed by sweeping or using an industrial broom.

    Application Method :

    Application Method Textured System
    • Intermediate coat is applied with MegaZemin Z501, which is mixed with filler at the ratio of 1:2.
    • The mixture of prepared Megazemin Z502 is poured onto the surface and spread to the surface with the help of a triangular toothed trowel.
    • It should be ensured that the textured coating forms a seamless layer on the surface by passing over each other perpendicularly with the coral roller.
    • Before the application of MegaZemin Z502, it is important to apply the intermediate application with MegaZemin Z501, which was selected in the same color in order to prevent color fluctuations on the surface and to ensure a high surface coverage.
    • Check the consumption table for the process steps.
    • As an alternative to the above application, 0.1 – 0.5 mm silica filler can be added to the Megazemin Z502 in a ratio of 1:2 to obtain a non-slip, blunted surface.

    Application Recommendations :
    • Materials to be used in order to reduce the negative effects of thermal difference should be brought to the application area before 24 hours.
    • It should be taken into consideration that pot life and working time of epoxy based products will be shortened at high temperatures and extended at low temperatures, depending on the ambient humidity and temperature.
    • In order for the application area to be opened to pedestrian traffic, it should be adhered to drying times after the product application is completed.
    • Ambient temperature and humidity should be kept under control during opening to pedestrian traffic.
    • The mixture should never be made by hand.
    • Smoothness should be provided to prevent water accumulation on the application surface.
    • After mixing, the product should be used within its pot life. During the application, products that have expired their pot life should never be used.
    • During application, no foreign materials should be added to the mixture, except for the components of the product and the recommended filler.
    • Only K907 filler should be added to the mixture, and the recommended ratios should not be exceeded.
    • It should not be applied on non-solid surfaces. The stability and bearing of old surfaces should be checked before application.
    • Before, during and after application, the surface should be protected from air currents; it should be protected from contact with water and condensation for 24 hours.
    • It should not be applied on surfaces that are frozen, unfreezing or in danger of frost within 24 hours.
    • It should be noted that in hot weather the material is not exposed to direct sun rays.
    • Application should not be done on hot surfaces with extreme wind or direct sun, if there is an obligation to apply in these environments, the environment and surface should be ready for application before starting.
    • Call our technical support line for different surface applications. (PHONE: 444 4 595)

    Surface and ambient temperature
    Surface and ambient temperature must be between +10°C and +30°C.
    When deemed necessary, the environment should be heated with electrical heaters. It is not recommended to use heaters that work with the combustion system, since they may create pollution on the surface.